| “Moplen” RP225M is a controlled rheology medium modified propylene random copolymer for manufacturing high transparent cast films. The product contains slip and anti-block agents. It offers good processability, excellent clarity and gloss and exhibits very good heat weldability. Main applications are packaging of foodstuffs, packaging of stationary, shirts and hosiery. It is also suitable for production of stationary folders. “Moplen” RP225M is suitable for food contact. For regulatory information please refer to “Moplen” RP225M Product Stewardship Bulletin ( PSB ).&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,Good surface appearance,Smoothness,Controllable rheological,High anti-blocking,Food contact compliance,Random copolymer,Welding |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 8.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 700 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 23.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 12 | % | ISO 527-2/50 |
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic, casting thin films | 0.20 | ASTM D1894 | |
| Compared to itself – static, cast thin films | 0.20 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Secant modulus | |||
| MD, 50 µ m, cast thin film | 560 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 50 µ m, extruded film | 19.4 | MPa | ASTM D882 |
| MD, fracture, 50 µ m, extruded film | 38.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, yield, 50 µ m, extruded film | 7.6 | % | ASTM D882 |
| MD, fracture, 50 µ m, extruded film | 740 | % | ASTM D882 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0℃ | 1.5 | kJ/m² | ISO 179/1eA |
| 23℃ | 9.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 60.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 120 | ℃ | ISO 306/A50 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 50.0 µ m, cast thin film | 89 | ASTM D2457 | |
| Haze | |||
| 50 µ m, cast thin film | < 1.5 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.98 in/min |
| 3. 1.2 in/min |
| 4. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |