| Elvaloy® AC 3117 is a copolymer of ethylene and butyl acrylate. It is available in pellet form for use in conventional extrusion equipment designed to process polyethylene type resins. 17% Butyl Acrylate&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EBA |
| Material Status | Commercial: Active |
| Features | Copolymer |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.924 | g/cm³ | ASTM D792 |
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.5 | g/10min | ISO 1133 |
| 190℃，2.16kg | 1.5 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 60.0 | ℃ | ASTM D1525 |
| Vicat Softening Temp | 60.0 | ℃ | ISO 306 |
| Melting peak temperature | 99.0 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 99.0 | ℃ | ISO 3146 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Butyl Acrylate Content | 17.0 | wt% |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 135 | °C | |
| Barrel 2 zone temperature | 160 | °C | |
| Barrel 3 zone temperature | 185 | °C | |
| Barrel 4 zone temperature | 185 | °C | |
| Barrel 5 zone temperature | 185 | °C | |
| Connector temperature | 185 | °C | |
| Melt temperature | 160 to 235 | °C | |
| Nozzle temperature | 185 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |