| About |
|---|
| PPR PA6602 is a Polyamide 66 (Nylon 66) product filled with 33% glass fiber. It is available in North America. Primary characteristic: heat stabilizer.&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.20 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 179 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| Bending modulus | |||
| tangent | 8960 | MPa | ASTM D790 |
| bending strength | 255 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 80 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 260 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 252 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 to 82 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 238 to 282 | °C | |
| Barrel middle temperature | 249 to 293 | °C | |
| Barrel front temperature | 249 to 293 | °C | |
| Nozzle temperature | 243 to 288 | °C | |
| Processing (melt) temperature | 254 to 299 | °C | |
| Mold temperature | 66 to 93 | °C | |
| Injection pressure | 13.8 to 103 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |