| About |
|---|
| Alathon L5008 is a bimodal, high molecular weight, high density polyethylene resin with excellent processing characteristics. L5008 is selected by customers for demanding pressure pipe applications. When combined with an approved color or black masterbatch at the correct use level, L5008 may meet the following standards or requirements (see Technical Data Sheet for limitations and more information): ASTM D3350 Cell Classifications: PE445564C, PE445564E, PE445565C, PE445565E NSF Standard 14 and Standard 61 for Potable Water Pipe and Fittings NSF Standard 358-1 for PE Pipe and Fittings for “Geothermal” Heat Pump Systems PE80 per ISO 9080 & ISO 12162 Plastics Pipe Institute (PPI) PE 3408 and PE4608 per PPI TR-3&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High molecular weight,Copolymer,Bimodal molecular weight distribution |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.070 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 16 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 34.3 | MPa | ASTM D638 |
| yield | 24.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 640 | % | ASTM D638 |
| Bending modulus | |||
| 2% secant | 972 | MPa | ASTM D790 |
| Fundamentals of Hydrostatic Design | ASTM D2837 | ||
| 23℃ | 11.0 | MPa | ASTM D2837 |
| 60℃ | 6.89 | MPa | ASTM D2837 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 68.0 | ℃ | ASTM D648 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| DSC Induction Temperature | 267 | ℃ | ASTM D3350 |
| Slow crack propagation PENT | |||
| 80℃ | > 100 | hr | ASTM F1473 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. 2.4 MPa |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |