Polifil® ABS GFABS-20

About
Polifil ® GFABS series compounds combine the most desirable properties of both components – allowing for enhanced processability and toughness together with the stiffness of glass. These compounds are used in firearms, automotive applications and household appliances. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application.&&

About

Polifil ® GFABS series compounds combine the most desirable properties of both components – allowing for enhanced processability and toughness together with the stiffness of glass. These compounds are used in firearms, automotive applications and household appliances. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application.&&

Product Description
Generic	ABS
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,Good flexibility
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.22	g/cm³	ASTM D792
Melt Flow Rate
230℃，2.16kg	3.0 to 10	g/10min	ASTM D1238
Shrinkage rate
MD：3.2 mm	0.20	%	ASTM D955
Water absorption rate
24hr	0.20	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	64	J/m	ASTM D256
Drop hammer impact
23℃，12.7 mm	0.452	J	ASTM D3029

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed	104	℃	ASTM D648
1.8 MPa, unannealed	98.9	℃	ASTM D648

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	114		ASTM D785
Tensile modulus
23℃	6210	MPa	ASTM D638
tensile strength
23℃	75.8	MPa	ASTM D638
Tensile strain			ASTM D638
Yield, 23 ℃	2.0	%	ASTM D638
Fracture, 23 ℃	2.0	%	ASTM D638
Bending modulus
Tangent, 23 ℃	5520	MPa	ASTM D790
bending strength
23℃	107	MPa	ASTM D790

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	82	°C
Drying time	2.0	hr
Barrel rear temperature	204 to 216	°C
Barrel middle temperature	210 to 221	°C
Barrel front temperature	221 to 232	°C
Nozzle temperature	227 to 232	°C
Processing (melt) temperature	218 to 271	°C
Mold temperature	38 to 66	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.