Polyglue® HB520

About
HB520 is anhydride grafted polyethylene. It is useful in pellet form for use conventional extrusion and co- extrusion equipment designed to process polyethylene resins. Usually this materials is used in multi-layered barrier film, tube and sheet production. HB520 is developed for polyamide (Nylon) based barrier film. HB520 is suitable for multi-layer blown film. Based on HDPE, this adhesive is used for the tie layer between PE and barrier materials.&&

About

HB520 is anhydride grafted polyethylene. It is useful in pellet form for use conventional extrusion and co- extrusion equipment designed to process polyethylene resins. Usually this materials is used in multi-layered barrier film, tube and sheet production. HB520 is developed for polyamide (Nylon) based barrier film. HB520 is suitable for multi-layer blown film. Based on HDPE, this adhesive is used for the tie layer between PE and barrier materials.&&

Product Description
Supplier	HYUNDAI EP
Generic	PE
Material Status	Commercial: Active
Availabilitys	Asia Pacific
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.957	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	0.50	g/10min	ASTM D1238

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -70.0	℃	ASTM D746
Vicat Softening Temp	125	℃	ASTM D1525
Melting peak temperature	132	℃	ASTM D3418

Supplementary information	Nominal value	Unit	Test method
Adhesive strength	> 2.0	kN/m	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	65		ASTM D2240
tensile strength
fracture	29.4	MPa	ASTM D638
Tensile strain
fracture	650	%	ASTM D638

Process Conditions
Squeeze description	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method

Barrel 1 zone temperature	180 to 190	°C
Barrel 2 zone temperature	190 to 200	°C
Barrel 3 zone temperature	200 to 210	°C
Barrel 4 zone temperature	210 to 220	°C
Barrel 5 zone temperature	210 to 220	°C
Melt temperature	180 to 220	°C
Nozzle temperature	210 to 220	°C
Screw length to diameter ratio	24.0:1.0

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.