| About |
|---|
| Rotec® ASA E 510 is an Acrylonitrile Styrene Acrylate (ASA) material. It is available in Europe for extrusion or injection molding. Important attributes of Rotec® ASA E 510 are: Flame Rated Impact Resistant Weather Resistant&& |
| Product Description | |
|---|---|
| Generic | ASA |
| Material Status | Commercial: Active |
| Features | High impact resistance,HB |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 12 | g/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.60 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.30 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 1900 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 40.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 23 ℃ | 20 | % | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 2000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 60.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 80.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 90.0 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 9.5E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.17 | W/m/K | ISO 8302 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | < 80.0 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Proposed maximum recycled material ratio | 5 | % | |
| Barrel rear temperature | 210 to 250 | °C | |
| Barrel middle temperature | 210 to 250 | °C | |
| Barrel front temperature | 210 to 250 | °C | |
| Processing (melt) temperature | < 260 | °C | |
| Mold temperature | 40.0 to 80.0 | °C | |
| Injection speed | 快速 | ||
| Drying temperature | < 80.0 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.050 | % | |
| Barrel 1 zone temperature | 190 to 210 | °C | |
| Barrel 2 zone temperature | 190 to 210 | °C | |
| Barrel 3 zone temperature | 190 to 210 | °C | |
| Barrel 4 zone temperature | 190 to 210 | °C | |
| Barrel 5 zone temperature | 190 to 210 | °C | |
| Melt temperature | < 245 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |