Eltex® PF6130LA

About
Eltex ® PF6130LA is particularly suitable for high performance cast stretch film applications, in both monolayer and co-extruded structures. It is designed for applications which require a very low level of gels. It also can be used for the production of artificial grass monofilaments. Benefits and Features Eltex ® PF6130LA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. Eltex® PF6130LA offers the following properties: High stretchability in cast film applications High holding force Good web stability during extrusion High output rates Excellent overall film appearance and surface finish Low level of gels Very high puncture resistance We recommend that you consult your INEOS technical representative for further advice on the use of Eltex® PF6130LA.&&

About

Eltex ® PF6130LA is particularly suitable for high performance cast stretch film applications, in both monolayer and co-extruded structures. It is designed for applications which require a very low level of gels. It also can be used for the production of artificial grass monofilaments. Benefits and Features Eltex ® PF6130LA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. Eltex® PF6130LA offers the following properties: High stretchability in cast film applications High holding force Good web stability during extrusion High output rates Excellent overall film appearance and surface finish Low level of gels Very high puncture resistance We recommend that you consult your INEOS technical representative for further advice on the use of Eltex® PF6130LA.&&

Product Description
Supplier	INEOS
Generic	mLLDPE
Material Status	Commercial: Active
Features	Good surface appearance,Low speed solidification point,Inoxidizability,Good Tensile Strength,Low density,Copolymer,Puncture Resistant,Hexene copolymers
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.918	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	3.5	g/10min	ISO 1133

film	Nominal value	Unit	Test method
film thickness
test	20	µm
Tensile modulus			ISO 1184
1% secant, MD, 20 µ m	115	MPa
1% secant, TD, 20 µ m	120	MPa
tensile strength			ISO 1184
MD, fracture, 20 µ m	40.0	MPa
TD, fracture, 20 µ m	20.0	MPa
Tensile strain			ISO 1184
MD, fracture, 20 µ m	300	%
TD, fracture, 20 µ m	400	%
Drop hammer impact
20 µm	600	g	ASTM D1709-A
Elmandorf tear strength			ASTM D1922
MD：25 µm	260	g
TD：25 µm	430	g

optical performance	Nominal value	Unit	Test method
gloss
45°，20 µm	93		ASTM D2457
Haze
20 µm	1.0	%	ASTM D1003

Supplementary information	Nominal value	Unit	Test method
Puncture resistance	28.0	Ncm/µ	Internal Method

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	230 to 280	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.