| Peelable Seal Barrier Coated Film Biaxially oriented polypropylene (BOPP) film coated on both sides with an aqueous dispersion of polyvinylidene chloride (PVdC). RXP125 is recommended for use in printed or plain applications in the bakery or confectionery industries. Particularly suitable for V.F.F. applications.&& |
| Product Description | |
|---|---|
| Generic | PP Alloy |
| Material Status | Commercial: Active |
| Features | Good heat sealing,High impact resistance,Good Printability,Low odor,Food contact compliance,Poor moisture permeability,Antistatic property,low-temperature impact resistance,Puncture Resistant |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | Internal Method | ||
| MD：121℃，1 min | 4.0 | % | Internal Method |
| MD：129℃，1 min | 7.0 | % | Internal Method |
| TD：129℃，1 min | 1.0 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.25 | ASTM D1894 | |
| With oneself – static | 0.25 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 3200 | µm | |
| Sealing emphasis | 0.14 | N/mm | Internal Method |
| Initial sealing temperature | 104 to 146 | ℃ | Internal Method |
| Oxygen permeability | |||
| 25℃，0% RH | 0.38 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water vapor transmittance | |||
| 38℃，90% RH | 3.9 | g/m²/24 hr | ASTM F1770 |
| dosage | 33.6 | m²/kg | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | > 100 | ASTM D2457 | |
| Haze | 3.0 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |