| About |
|---|
| High desnity polyethylene with narrow molar mass distribution, containing a medium amount of wood fibers and functional additives. Recommended for the production of injection moulded articles.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Renewable resources,Weight distribution |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 6.0 to 7.5 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1920 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 25.0 | MPa | ISO 527-2 |
| fracture | 24.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 6.0 | % | ISO 527-2 |
| fracture | 7.0 | % | ISO 527-2 |
| Bending modulus | 1950 | MPa | ISO 178 |
| bending strength | |||
| 3.50% strain | 29.0 | MPa | ISO 178 |
| Fracture bending strain | No Break | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.6 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 12 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 130 to 145 | ℃ | ISO 3146 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Measured on injection moulded specimen |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |