Amodel® AS-1935 HS

About
Amodel® AS-1935 HS is a 35% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material exceeds the performance required by the automotive industry for polymeric materials exposed to antifreeze at 226°F (108°C), even when tested at 275°F (135°C). Former PXM-12091 Black: AS-1935 HS BK 328&&

About

Amodel® AS-1935 HS is a 35% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material exceeds the performance required by the automotive industry for polymeric materials exposed to antifreeze at 226°F (108°C), even when tested at 275°F (135°C). Former PXM-12091 Black: AS-1935 HS BK 328&&

Product Description
Supplier	Solvay
Generic	PPA
Material Status	Commercial: Active
Features	Good Rigidity,Ethylene glycol,Good flexibility,Good Dimensional Stability,Antifreeze,High Heat Resistance,Solvent resistance,Heat Stabilized
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.49	g/cm³	ISO 1183/A
Shrinkage rate
TD	0.60	%	ASTM D955
MD	0.20	%	ASTM D955

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	12500	MPa	ASTM D638
Tensile modulus	12600	MPa	ISO 527-2/1A/1
tensile strength
fracture	210	MPa	ISO 527-2
fracture	205	MPa	ASTM D638
Tensile strain
fracture	2.2	%	ASTM D638
fracture	2.2	%	ISO 527-2
Bending modulus	11300	MPa	ASTM D790
Bending modulus	11500	MPa	ISO 178
bending strength	300	MPa	ISO 178
fracture	275	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength	8.0	kJ/m²	ISO 179-1eA
Charpy Unnotch Impact strength	66	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch	65	J/m	ASTM D256
Impact strength of cantilever beam notch	8.5	kJ/m²	ISO 180-1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	290	℃	ISO 75-2/Af
Melting temperature	323	℃	ISO 11357-3

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	121	°C
Drying time	4.0	hr
Recommended maximum moisture content	0.10	%
Hopper temperature	79	°C
Barrel rear temperature	313 to 330	°C
Barrel front temperature	326 to 339	°C
Processing (melt) temperature	330 to 350	°C
Mold temperature	150	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.