| About |
|---|
| The Sarlink EE-2200 series UV Resistant extrusion grades suitable for automotive exterior applications.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High density |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.40 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw’s A | 43 | ||
| Shore A, 15 seconds | 40 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| TD, 100% strain | 0.758 | MPa | |
| MD, 100% strain | 1.17 | MPa | |
| tensile strength | ASTM D412 | ||
| TD, fracture | 5.79 | MPa | |
| MD, fracture | 3.59 | MPa | |
| Tensile strain | ASTM D412 | ||
| TD, fracture | 910 | % | |
| Flow rate, fracture | 720 | % | |
| tear strength | |||
| TD | 20.8 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395 | ||
| 23℃，22 hr | 11 | % | |
| 70℃，22 hr | 26 | % | |
| 125℃，70 hr | 78 | % |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Barrel rear temperature | 199 to 210 | °C | |
| Barrel middle temperature | 204 to 216 | °C | |
| Barrel front temperature | 210 to 221 | °C | |
| Nozzle temperature | 216 to 227 | °C | |
| Processing (melt) temperature | 216 to 227 | °C | |
| Mold temperature | 35.0 to 65.6 | °C | |
| Injection pressure | 1.38 to 6.89 | MPa | |
| Barrel 1 zone temperature | 193 to 204 | °C | |
| Barrel 2 zone temperature | 199 to 210 | °C | |
| Barrel 3 zone temperature | 204 to 216 | °C | |
| Barrel 5 zone temperature | 210 to 221 | °C | |
| Nozzle temperature | 216 to 227 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |