| About |
|---|
| Toraycon® 5101G-30U is a Polybutylene Terephthalate (PBT) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Typical application: Automotive. Characteristics include: Flame Rated Impact Resistant&& |
| Product Description | |
|---|---|
| Supplier | Toray |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | High impact resistance,Hydrolysis stability,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ISO 1183 |
| Shrinkage rate | Internal Method | ||
| TD：3.0 mm | 1.0 | % | Internal Method |
| MD：3.0 mm | 0.40 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.070 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 14 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 65 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 220 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 205 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD：-30~100℃ | 4.2E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric constant | IEC 60250 | ||
| 23 ℃，50 Hz | 3.90 | IEC 60250 | |
| 23 ℃，1 kHz | 3.70 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 23℃，50 Hz | 2.0E-3 | IEC 60250 | |
| 23℃，1 MHz | 0.020 | IEC 60250 | |
| Arc resistance | 130 | sec | IEC 60950 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Rod flow length | |||
| 250℃，1.00 mm | 6.70 | cm | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 60 | ISO 2039-2 | |
| Tensile modulus | |||
| 23℃ | 8500 | MPa | ISO 527-2 |
| tensile strength | |||
| 23℃ | 130 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 8000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 205 | MPa | ISO 178 |
| friction coefficient | 0.19 | ||
| vs. Metal | 0.15 | Suzuki Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 80×80×3mm |
| 3. Without Lubrication |
| 4. 60% RH |
| 5. Tungsten Electrode |
| 6. 93 MPa |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |