| Orgalloy® LT 5050 NAT T6L resin is a very flexible polyamide alloys. Outstanding properties: easy to process, low moisture absorption, good mechanical properties at low temperature. Orgalloy® LT 5050 NAT T6L resin demonstrates a good balance of properties: high flexibility (500 MPa), good thermal performance and ductility at low temperatures. It is a barrier to HFC gas and resistant to oils making it well suited to the extrusion of tubes or film for air conditioning hoses.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA6 Alloy |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good flexibility,Ductility,Antifreeze,High Flexibility,Grease resistance,Block resin,Low moisture absorption,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | |
| Melt Volume Rate | |||
| 235℃，5 kg | 2.00 | cm³/10min | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | — | MPa | |
| tensile strength | |||
| 50% strain | — | MPa | |
| Tensile strain | |||
| fracture | — | % | |
| Tensile creep modulus | |||
| 1 hr | — | MPa | |
| 1000 hr | — | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 75 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 75.0 | ℃ | |
| Melting temperature | 220 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 1.7E-4 | 1/℃ | |
| TD | 1.8E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | — | ohms | |
| Volume resistivity | — | ohms·cm | |
| Dielectric strength | 36 | kV/mm | |
| Relative permittivity | |||
| 100 Hz | — | ||
| 1 MHz | — | ||
| Dissipation factor | |||
| 100 Hz | — | ||
| 1 MHz | — | ||
| Compared to the leakage tracing index | — | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.6 mm | HB | ||
| 3.2 mm | HB |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |