| About |
|---|
| LUTENE FB0800 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of greenhouse film. LUTENE FB0800 have the excellent mechanical properties and optical properties make suitable for manufacture of greenhouse films. LUTENE FB0800 contains neither slip agent nor antiblock agent and antiblock agent for agricultural films . Applications: Large width film for greenhouse, Tunnel films.&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Optical performance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | 0.15 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | 50 to 300 µm | ||
| tensile strength | ASTM D882 | ||
| MD, fracture | 21.7 | MPa | ASTM D882 |
| TD, fracture | 20.7 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 550 | % | ASTM D882 |
| TD, fracture | 650 | % | ASTM D882 |
| Drop hammer impact | 230 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD | 280 | g | ASTM D1922 |
| TD | 350 | g | ASTM D1922 |
| Oxygen permeability | 2000 | cm³/m²/24 hr | Internal Method |
| Water vapor permeability | 12 | g/m²/24 hr | Internal Method |
| Nitrogen transfer rate | 3500 | cm³/m²/24 hr | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 94.0 | ℃ | ASTM D1525 2 |
| Melting temperature | 110 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | 8.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 170 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |