| About |
|---|
| Sarlink TPE OM series are high performance specialty thermoplastic elastomers designed for automotive applications requiring excellent bondability to engineered resin substrates. Sarlink TPE OM-1150N is a medium hardness, medium density, opaque grade with good UV resistance that exhibits excellent adhesion to ABS, PC, and PC/ABS.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good bond,Moderate liquidity,Solvent resistance,Agglomerability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.998 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 15 | g/10min | ASTM D1238 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| TD, 100% strain | 1.48 | MPa | ASTM D412 |
| MD, 100% strain | 1.65 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| TD, 300% strain | 2.90 | MPa | ASTM D412 |
| MD, 300% strain | 3.27 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| fracture | 5.67 | MPa | ASTM D412 |
| MD, fracture | 5.87 | MPa | ASTM D412 |
| Tensile strain | ASTM D412 | ||
| fracture | 550 | % | ASTM D412 |
| Flow rate, fracture | 540 | % | ASTM D412 |
| Compression deformation | ASTM D395B | ||
| 23℃，22 hr | 42 | % | ASTM D395B |
| 70℃，22 hr | 91 | % | ASTM D395B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore A, 1 second, injection molding | 45 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 55 | ASTM D2240 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Adhesive strength | |||
| Cohesive Failure | 51 | N | |
| Adhesion to ABS | |||
| Adhesion to PC | |||
| Adhesion to PC/ABS |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 138 to 188 | °C | |
| Barrel middle temperature | 154 to 199 | °C | |
| Barrel front temperature | 154 to 216 | °C | |
| Nozzle temperature | 154 to 221 | °C | |
| Processing (melt) temperature | 166 to 221 | °C | |
| Mold temperature | 10 to 32 | °C | |
| Injection pressure | 1.38 to 5.52 | MPa | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 0.172 to 0.862 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Cushion | 3.81 to 25.4 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C, 20 in/min |
| 3. Type 1 |
| 4. Aged for 0 hr at 73°F |
| 5. Aged for 48 hr at 73°F |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |