Petrothene® GA601

About
The PETROTHENE GA 601 series resins is pelletized, linear low density polyethylenes for applications that require maximum strength and toughness. These products offer excellent additive homogeneity, require no transfer equipment modifications, and facilitate clean and safe handling. Applications include heavy duty shipping sacks, prime liners, commercial and industrial packaging, as well as food and consumer packaging. The GA 601 series resins offers enhanced film strength, drawdown, toughness and heat seal strength. In addition, these resins have excellent low temperature resistance for applications such as stretch film and frozen food packaging. The GA 601 series resins can be purchased without additives, fully formulated with slip and antiblock or containing a processing aid.&&

About

The PETROTHENE GA 601 series resins is pelletized, linear low density polyethylenes for applications that require maximum strength and toughness. These products offer excellent additive homogeneity, require no transfer equipment modifications, and facilitate clean and safe handling. Applications include heavy duty shipping sacks, prime liners, commercial and industrial packaging, as well as food and consumer packaging. The GA 601 series resins offers enhanced film strength, drawdown, toughness and heat seal strength. In addition, these resins have excellent low temperature resistance for applications such as stretch film and frozen food packaging. The GA 601 series resins can be purchased without additives, fully formulated with slip and antiblock or containing a processing aid.&&

Product Description
Supplier	LyondellBasell
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,Good heat sealing,Good dissection,Food contact compliance
Availabilitys	North America,Latin America,Asia Pacific,Europe
Process Methods	Film extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.918	g/cm³	ASTM D1505
Melt Flow Rate
190℃，2.16kg	1.0	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
film thickness
test	25	µm
Secant modulus
1% secant, TD, 25 µ m	224	MPa	ASTM D882
1% secant, MD, 25 µ m	200	MPa	ASTM D882
tensile strength
TD, fracture, 25 µ m	42.1	MPa	ASTM D882
MD, fracture, 25 µ m	55.8	MPa	ASTM D882
Tensile strain
TD, fracture, 25 µ m	700	%	ASTM D882
MD, fracture, 25 µ m	580	%	ASTM D882
Drop hammer impact
25 µ m, blow molded film	190	g	ASTM D1709-A
Total energy impact
25 µ m, blow molded film	2.44	J	ASTM D4272
Elmandorf tear strength
MD，25 µm	330	g	ASTM D1922
tear strength
TD，25 µm	650	g	ASTM D1922

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	105	℃	ASTM D1525

optical performance	Nominal value	Unit	Test method
gloss
45 °, 25.4 µ m, blow molded film	35		ASTM D2457
Haze
25.4 µ m, blow molded film	22	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	204 to 232	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.