| About |
|---|
| Torayca® 2701T-30V is a Polyamide 610 (Nylon 610) product filled with 30% carbon fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Toray |
| Generic | PA610 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific,Europe,North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Shrinkage rate | Internal Method | ||
| TD：3.0 mm | 0.50 | % | Internal Method |
| MD：3.0 mm | 0.10 | % | Internal Method |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.1 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 264 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.2 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 20000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 398 | MPa | ISO 178 |
| Wear amount | |||
| vs. S45C | 0.300 | mg/hr | Suzuki Method |
| friction coefficient | |||
| vs. S45C | 0.36 | Suzuki Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 13 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 210 | ℃ | ISO 75-2/A |
| Melting temperature | 225 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD | 1.5E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+3 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 80x80x3mm |
| 3. 1MPa, 0.33 m/s |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |