| Amodel AE-8935 is a 35% glycol resistant glass-reinforced heat stabilized polyphtalamide (PPA) resin designed to work in the modern automotive electrical environment. It is distinguished by a high heat deflection temperature, high flexural modulus, high tensile strength and low moisture absorbtion. This grade displays excellent resistance to cracks which may occur during thermal shock cycling. Black: AE-8935 BK902&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good Dimensional Stability,High Heat Resistance,Solvent resistance,Low moisture absorption,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ISO 1183/A |
| Shrinkage rate | |||
| TD | 0.80 | % | ASTM D955 |
| MD | 0.30 | % | ASTM D955 |
| Water absorption rate | |||
| balance | 0.16 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 12600 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 220 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.4 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 12200 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 300 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 96 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 290 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Compared to the leakage tracing index | > 600 | V | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.030 to 0.060 | % | |
| Barrel rear temperature | 316 to 330 | °C | |
| Barrel middle temperature | 316 to 330 | °C | |
| Barrel front temperature | 324 to 340 | °C | |
| Processing (melt) temperature | 330 to 352 | °C | |
| Mold temperature | 150 to 165 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |