| About |
|---|
| LEXAN *DX07350 resin is a glass filled, Non-brominated & Non-chlorinated flame retardant polycarbonate. High stiffness and good flow.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good liquidity,Halogen free,Flame Characteristics,HB,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume Rate | |||
| 280℃，2.16 kg | 21.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.35 to 0.45 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.090 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.050 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 3.3 | kJ/m² | |
| 23℃ | 3.5 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 61 | kJ/m² | |
| 23℃ | 75 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 35 | J/m | ASTM D256 |
| 23℃ | 42 | J/m | ASTM D256 |
| -30℃ | 4.6 | kJ/m² | ISO 180-1A |
| 23℃ | 4.7 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 47 | kJ/m² | |
| 23℃ | 50 | kJ/m² | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 11.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 102 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 104 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B120 | 112 | ℃ | ASTM D1525, ISO 306/B120 13 18 |
| B50 | 109 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | ASTM E831, ISO 11359-2 | ||
| MD：-40~40℃ | 3.7E-5 | 1/℃ | |
| TD：-40~40℃ | 6.6E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Pencil hardness | ASTM D3363 | ||
| — | F | ||
| — | HB | ||
| Tensile modulus | |||
| — | 4700 | MPa | ASTM D638 |
| — | 4800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 65.0 | MPa | ASTM D638 |
| yield | 68.0 | MPa | ISO 527-2/5 |
| fracture | 55.0 | MPa | ASTM D638 |
| fracture | 54.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 4.0 | % | ASTM D638 |
| yield | 3.8 | % | ISO 527-2/5 |
| fracture | 5.0 | % | ASTM D638 |
| fracture | 4.8 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 4200 | MPa | ASTM D790 |
| — | 4600 | MPa | ISO 178 |
| bending strength | |||
| — | 120 | MPa | ISO 178 |
| Yield, 50 mm span | 116 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80.0 to 90.0 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60.0 to 80.0 | °C | |
| Barrel rear temperature | 250 to 280 | °C | |
| Barrel middle temperature | 260 to 290 | °C | |
| Barrel front temperature | 270 to 300 | °C | |
| Nozzle temperature | 270 to 290 | °C | |
| Processing (melt) temperature | 270 to 300 | °C | |
| Mold temperature | 60.0 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |