Braskem PE LL5400S

About
LL5400S is a Linear Low Density Polyethylene developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. Applications: Liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes. Process: Recommended processing conditions for film extrusion about 170 – 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee.&&

About

LL5400S is a Linear Low Density Polyethylene developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. Applications: Liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes. Process: Recommended processing conditions for film extrusion about 170 – 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee.&&

Product Description
Supplier	Braskem
Generic	Linear low density polyethylene
Material Status	Commercial: Negative
Features	Excellent Processability,Optical performance,Low speed solidification point,Inoxidizability
Availabilitys	Latin America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.918	g/cm³	ASTM D1505
Melt Flow Rate
190℃，2.16kg	1.0	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
tensile strength			ASTM D882
MD, fracture, 38 µ m, blow molded film	40.0	MPa	ASTM D882
TD, fracture, 38 µ m, blow molded film	30.0	MPa	ASTM D882
Tensile strain			ASTM D882
MD, fracture, 38 µ m, blow molded film	1100	%	ASTM D882
TD, fracture, 38 µ m, blow molded film	1400	%	ASTM D882
Bending modulus			ASTM D790
1% secant, MD, 38 µ m, blow molded film	170	MPa	ASTM D790
1% secant, TD, 38 µ m, blow molded film	200	MPa	ASTM D790
Drop hammer impact
38 µ m, blow molded film	120	g	ASTM D1709
Elmandorf tear strength			ASTM D1922
MD: 38 µ m, blow molded film	100	g	ASTM D1922
TD: 38 µ m, blow molded film	400	g	ASTM D1922

optical performance	Nominal value	Unit	Test method
gloss
60 °, 38.0 µ m, blow molded film	110		ASTM D2457
Haze
38 µ m, blow molded film	10	%	ASTM D1003

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.