Stanyl® TW241F10

About
50% Glass Reinforced, Heat Stabilized, Lubricated&&

Product Description
Supplier	DSM
Generic	PA 46
Material Status	Commercial: Active
Features	Heat Stabilized
Availabilitys	Europe,Asia Pacific,North America

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
	16000	MPa	ISO 527-1/-2
120°C	8500	MPa	ISO 527-1/-2
160°C	7200	MPa	ISO 527-1/-2
180°C	6600	MPa	ISO 527-1/-2
200°C	6000	MPa	ISO 527-1/-2
Tensile stress
	250	MPa	ISO 527-1/-2
Fracture, 120 ° C	140	MPa	ISO 527-1/-2
Fracture, 160 ° C	120	MPa	ISO 527-1/-2
Fracture, 180 ° C	110	MPa	ISO 527-1/-2
Fracture, 200 ° C	100	MPa	ISO 527-1/-2
elongation at break	2.7	%	ISO 527-1/-2
Tensile strain
Fracture, 120 ° C	5	%	ISO 527-1/-2
Fracture, 160 ° C	5.5	%	ISO 527-1/-2
Fracture, 180 ° C	5.5	%	ISO 527-1/-2
Fracture, 200 ° C	6	%	ISO 527-1/-2
Bending modulus
	15000	MPa	ISO 178
120°C	7300	MPa	ISO 178
160°C	6500	MPa	ISO 178
bending strength
	380	MPa	ISO 178
120°C	180	MPa	ISO 178
160°C	150	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength
23°C	100	kJ/m²	ISO 179/1eU
-30°C	90	kJ/m²	ISO 179/1eU
Charpy Notched Impact Strength
23°C	16	kJ/m²	ISO 179/1eA
-30°C	14	kJ/m²	ISO 179/1eA
Impact strength of cantilever beam notch
23°C	16	kJ/m²	ISO 180/1A
-40°C	14	kJ/m²	ISO 180/1A

THERMAL	Nominal value	Unit	Test method
Melting temperature
10°C/min	295	℃	ISO 11357-1/-3
Hot deformation temperature
1.80 MPa	290	℃	ISO 75-1/-2
0.45 MPa	290	℃	ISO 75-1/-2
Linear coefficient of thermal expansion
MD	2.5E-5	℃	ISO 11359-1/-2
TD	4.0E-5	℃	ISO 11359-1/-2
Relative temperature index
Electrical characteristics, 0.75mm	65	℃	UL 746B
Heat index
5000 hrs	177	℃	IEC 60216
5000 hrs	177	℃	ISO 527-1/-2

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	1.0E+12	ohms·cm	IEC 62631-3-1
Dielectric strength	30	kV/mm	IEC 62631-3-1
Compared to the leakage tracing index	300	V	IEC 60112
Dielectric constant
100Hz	4.3		IEC 62631-2-1
1MHz	4		IEC 62631-2-1

Process Conditions
Injection	Nominal value	Unit	Test method
drying temperature	80.0	°C
Drying time	4.0 to 8.0	hr
Temperature at the rear of the barrel	280 to 320	°C
Temperature in the middle of the barrel	300 to 320	°C
Front temperature of material barrel	300 to 320	°C
Nozzle temperature	300 to 320	°C
Processing (melt) temperature	305 to 320	°C
Mold temperature	80.0 to 120	°C
Injection speed	中等偏快
Back pressure	2.00 to 10.0	MPa
Screw compression ratio	2.5:1.0

Notes
1. Typical properties: these are not to be construed as specifications.
2. 10°C/min
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.