3M™ Dyneon™ TFM™ Modified PTFE TFM 2070Z

About
3M™ Dyneon™ TFM™ Modified PTFE Fine Powder TFM 2070Z is a second generation emulsion PTFE grade for high-performance tubing of smaller dimensions. Special Features Meets ASTM D 4895 Type I, Grade 1, Class B classification High molecular weight PTFE powder produced by emulsion polymerisation Fine powder grade for medium to high reduction ratio (RR) range Isotropic mechanical properties in sintered tubes Very good weldability Low friction behaviour High flame retardance Smooth surfaces and high transparency High stress-cracking resistance High pressure resistance under surge stress Processing by standard paste extrusion method Excellent chemical inertness Exceptional temperature resistance Very good electrical properties&&

About

3M™ Dyneon™ TFM™ Modified PTFE Fine Powder TFM 2070Z is a second generation emulsion PTFE grade for high-performance tubing of smaller dimensions. Special Features Meets ASTM D 4895 Type I, Grade 1, Class B classification High molecular weight PTFE powder produced by emulsion polymerisation Fine powder grade for medium to high reduction ratio (RR) range Isotropic mechanical properties in sintered tubes Very good weldability Low friction behaviour High flame retardance Smooth surfaces and high transparency High stress-cracking resistance High pressure resistance under surge stress Processing by standard paste extrusion method Excellent chemical inertness Exceptional temperature resistance Very good electrical properties&&

Product Description
Generic	PTFE
Material Status	Commercial: Active
Features	Good Clarity,Good Electrical Properties,Low coefficient of friction,Flame Characteristics,High molecular weight,Welding,High ESCR
Availabilitys	North America,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	2.16	g/cm³	ISO 12086
Apparent density	0.46	g/cm³	ISO 60
Average particle size	350	µm	ISO 13320

film	Nominal value	Unit	Test method
tensile strength	36.0	MPa	ISO 527-3
Tensile strain
fracture	400	%	ISO 527-3

Supplementary information	Nominal value	Unit	Test method
Extrusion pressure
Reduction Ratio 400	19.0	MPa	ASTM D4895
Reduction Ratio	20.0:1.0 to 2000.0:1.0		Internal Method

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.