Borealis PP BH381MO

About
BH381MO is a heterophasic copolymer. This product is characterized by an optimum combination of very high stiffness and high impact strength. This grade uses Borealis Nucleation Technology (BNT) to increase productivity by cycle time reduction. BNT in combination with excellent stiffness and good flow properties creates a high potential for wall-thickness reduction. Products originating from this grade have very good demoulding properties, well-balanced mechanical properties, excellent dimension consistency with respect to different colors and good organoleptic properties. CAS-No. 9010-79-1&&

About

BH381MO is a heterophasic copolymer. This product is characterized by an optimum combination of very high stiffness and high impact strength. This grade uses Borealis Nucleation Technology (BNT) to increase productivity by cycle time reduction. BNT in combination with excellent stiffness and good flow properties creates a high potential for wall-thickness reduction. Products originating from this grade have very good demoulding properties, well-balanced mechanical properties, excellent dimension consistency with respect to different colors and good organoleptic properties. CAS-No. 9010-79-1&&

Product Description
Supplier	Borealis AG
Generic	PP copolymer
Material Status	Commercial: Active
Features	Good Rigidity,High impact resistance,Renewable resources,Good liquidity,Good sensory characteristics.,Copolymer
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.905	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	35	g/10min	ISO 1133
Shrinkage rate	1.0 to 2.0	%

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
50 mm	1700	MPa	ISO 527-2
tensile strength
yield	29.0	MPa	ISO 527-2/50
Tensile strain
yield	5.0	%	ISO 527-2/50
Bending modulus	1600	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-20℃	3.5	kJ/m²	ISO 179/1eA
23℃	6.5	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	105	℃	ISO 75-2/B

Process Conditions
injection	Nominal value	Unit	Test method
Processing (melt) temperature	210 to 280	°C
Mold temperature	10 to 30	°C
Hold pressure	20.0 to 50.0	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.