| About |
|---|
| GM5010T2 is a High Density Polyethylene compound specially developed for the manufacturing of extruded pipes. It is produced with bimodal technology and has high molar mass. It shows high mechanical properties and has excellent resistance to hydrostatic pressure and to stress cracking. This resin has MRS (Minimum Required Strength) of 8 MPa, according to ISO 9080, and is classified as PE 80, according to ISO 12162. GM5010T2 contains carbon black pigment that protects it against ultraviolet radiation action and photodegradation. Meets the requirements of NBR 15561:07 and ISO 4427:07. Application: Black PE 80 pressure pipes for water distribution, underwater emissaries and pressurized sewer systems; self-propelled irrigation pipes; jacketing of umbilical cables; risers and flowlines for oil filed platforms; pipes for mining. Process: Extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High molecular weight,Good tear strength,High density |
| Availabilitys | Latin America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.955 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，5.0kg | 0.45 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 2.00 mm, 100% non-ionic surfactant, molded, F50 | > 1000 | hr | ASTM D1693 |
| Carbon black content | 2.0 to 2.5 | % | ASTM D1603 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 62 | ASTM D2240 | |
| tensile strength | |||
| Fracture, molded | 34.0 | MPa | ASTM D638 |
| Yield, molding | 23.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 800 | % | ASTM D638 |
| Yield, molding | 9.1 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, molded | 1090 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| Compression Molding | 220 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, molded | 70.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 124 | ℃ | ASTM D1525 2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |