| About |
|---|
| Description RE400 is a propylene-ethylene random polypropylene designed for expanded beads of polypropylene (EPP). RE400 meets the demands of good foamability in batch-typed EPP process and fusion-bond between foamed beads in molding process. Characteristics Good Foamability Good Fusion-bond Properties Excellent UV Resistance Applications EPP bead for automobile and E&E.&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | PP copolymer |
| Material Status | Commercial: Negative |
| Features | Weather resistance is good,Foaming performance,Food contact compliance,Random copolymer |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 7.0 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 49 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 96.0 | ℃ | ASTM D648 |
| Melting temperature | 145 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 80 | ASTM D785 | |
| tensile strength | |||
| yield | 29.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 500 | % | ASTM D638 |
| Bending modulus | 932 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |