| ALTECH® ABS A 1000/188 is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by extrusion or injection molding and is available in Asia Pacific, Europe, or North America. Applications of ALTECH® ABS A 1000/188 include automotive, medical/healthcare and kitchenware. Characteristics include: Flame Rated RoHS Compliant Good Mold Release&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good stripping performance,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 220℃，10 kg | 7.00 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| — | 30 | kJ/m² | ISO 179/1eA |
| -40℃ | 15 | kJ/m² | ISO 179/1eA |
| -20℃ | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| — | 无断裂 | ISO 179/1eU | |
| -40℃ | 无断裂 | ISO 179/1eU | |
| -20℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 30 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 84.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 100 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ | IEC 60695-2-12 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 85.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1800 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 36.0 | MPa | ISO 527-2 |
| — | 40.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 15 | % | ISO 527-2 |
| Bending modulus | 1900 | MPa | ISO 178 |
| bending strength | ISO 178 | ||
| — | 60.0 | MPa | ISO 178 |
| 3.50% strain | 58.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Desiccant desiccant | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying time | |||
| Desiccant desiccant | 3.0 to 6.0 | hr | |
| Hot air dryer | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |