| AFFINITY™ SQ 1503 UE Polyolefin Plastomer is a Polyolefin Plastomer (POP) produced using INSITE™ Technology. AFFINITY SQ 1503 UE Polyolefin Plastomer is specifically designed for rotomoulding applications. It offers easy demoulding combined with flexibility and elastic recovery normally associated with polar copolymers such as EBA, EVA and plasticised PVC. Processing and Stabilisation: The inherently stable POP is further stabilised against heat and UV-radiation. The result is a wide processing latitude, good colour retention and long life expectancy. Availability: AFFINITY SQ 1503 UE Polyolefin Plastomer is available as free flowing powder ground to 500 micron. Applications: Buoys Fenders Road furniture Complies with: EU, No 10/2011 U.S. FDA FCN 424 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | POP |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 6.0 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | ASTM D1693 | ||
| 50 ℃, 10% emulsifier, molded | > 1000 | hr | ASTM D1693 |
| 50 ℃, 100% emulsifier, molded | > 1000 | hr | ASTM D1693 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile permanent deformation | |||
| 100% strain | 10 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Falling target impact | ISO 6603-2 | ||
| -20℃ | > 150 | J/cm | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 82.0 | ℃ | ISO 306/120 |
| Melting temperature | 97.0 | ℃ | DSC |
| Crystallization peak temperature | |||
| DSC | 80.0 | ℃ | DSC |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw A, molded | 92 | ISO 868 | |
| Shaw’s D, molded | 40 | ISO 868 | |
| tensile strength | ISO 527-2 | ||
| Yield, roll forming | 5.00 | MPa | ISO 527-2 |
| Yield, molding | 5.00 | MPa | ISO 527-2 |
| Fracture, roll forming | 19.0 | MPa | ISO 527-2 |
| Fracture, molded | 21.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| Fracture, roll forming | 1000 | % | ISO 527-2 |
| Fracture, molded | 1200 | % | ISO 527-2 |
| Bending modulus | ASTM D790 | ||
| 2% cut, roll forming | 70.0 | MPa | ASTM D790 |
| 2% cut, molded | 81.0 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rotational Molded |
| 3. Rotational Molded, No break |
| 4. Compression Molded, No break |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |