Promyde B33 LN is a high viscosity lubricated and nucleated Polyamide 6. CHARACTERISTICS Promyde B33 LN is a high viscosity polyamide 6 lubricated for injection moulding. APPLICATIONS Promyde B33 LN´s high viscosity provides a more resilient unfilled polyamide 6 over standard viscosity unfilled. Promyde B33 LN is suitable for the production of wheels and castors that support heavy loads. Its natural white colour and added nucleant for improved cooling make it an excellent alternative for stronger wheel and castor production over standard viscosity polyamide.&& |
Product Description | |
---|---|
Generic | PA6 |
Material Status | Commercial: Active |
Features | High Viscosity,Nucleation,Lubricating |
Availabilitys | Europe |
Process Methods | Injection Molding |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 1.13 | g/cm³ | ISO 1183 |
Shrinkage rate | |||
MD | 0.90-1.10 | % | ISO 294-4 |
TD | 0.80-1.10 | % | ISO 294-4 |
Water absorption rate | |||
23℃,24hr | 9.5 | % | ISO 62 |
23℃,50% RH | 3.0 | % | ISO 62 |
Viscosity measurement | 203 | ISO 307 | |
Melt Flow Rate | |||
275℃,5.0kg | 35 | g/10min | ISO 1133 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
tensile strength | |||
23℃ | 85.0 | MPa | ISO 527-2 |
Tensile strain | |||
Yield, 23 ℃ | 4.0 | % | ISO 527-2 |
Fracture, 23 ℃ | 50.0 | % | ISO 527-2 |
Tensile modulus | |||
23℃ | 3350 | MPa | ISO 527-2 |
bending strength | |||
23℃ | 110 | MPa | ISO 178 |
Bending modulus | |||
23℃ | 2850 | MPa | ISO 178 |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Hot deformation temperature | |||
0.45 MPa, unannealed | 197 | ℃ | ISO 75-2/Bf |
1.8 MPa, annealed | 65.0 | ℃ | ISO 75-2/Af |
Melting temperature | 222 | ℃ | ISO 3146 |
Linear coefficient of thermal expansion | |||
MD | 7.0E-7 | 1/℃ | ISO 11359-2 |
TD | 1.0E-5 | 1/℃ | ISO 11359-2 |
Electrical performance | Nominal value | Unit | Test method |
---|---|---|---|
Volumetric resistance | 1.0E+13 | Ω.cm | IEC 60093 |
Surface resistance | 1.0E+13 | Ω.cm | IEC 60093 |
Dielectric constant | |||
3.5 | 1 MHz | IEC 60250 | |
Dissipation factor | |||
Compared to the leakage tracing index | 600 | V | IEC 60112 |
FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
---|---|---|---|
Flame retardant level | |||
1.5mm | V-2 | UL 94 |
IMPACT | Nominal value | Unit | Test method |
---|---|---|---|
Charpy Unnotch Impact strength | |||
23℃ | NB | kJ/m² | ISO 179/1eU |
Charpy Notched Impact Strength | |||
23℃ | 5.70 | kJ/m² | ISO 179/1eA |
Process Conditions | |||
---|---|---|---|
injection | Nominal value | Unit | Test method |
Drying temperature | <=80.0 | °C | |
Drying time | 4-6 | Hr | |
Injection temperature | |||
Mold temperature | 40-80 | °C |
Notes |
---|
1. Typical properties: these are not to be construed as specifications. |
2. 0.079 in/min |
3. 10°C/min |
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |