| About |
|---|
| Hostacom ERC 450N is a 10% talc filled PP copolymer compound with superior flowability, low density, excellent scratch resistance, offering low odour and low emissions performances. Advanced technologies allowed for a significant reduction of mineral filler which contributed to the reduction of final part weight. This product is also available in other colors, new colors can be developed depending on customer requirements.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Excellent Processability,Good surface appearance,High impact resistance,High liquidity,Good liquidity,Good color stability,Low odor,Low density,Copolymer,Good wear resistance,High scratch resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.980 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 27 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | |||
| 23℃ | 1900 | MPa | ISO 178-A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 95.0 | ℃ | ISO 75-2/B |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.039 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |