| About |
|---|
| 15% Glass Reinforced, Heat Stabilized, Lubricated&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | Lubricating,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | g/cm³ | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 12 | % | |
| Equilibrium, 23 ℃, 50% RH | 3.2 | % | |
| Viscosity number | 150 | cm³/g | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 6100 | MPa | |
| 120℃ | 3000 | MPa | |
| 160℃ | 2650 | MPa | |
| 180℃ | 2500 | MPa | |
| 200℃ | 2350 | MPa | |
| tensile strength | |||
| fracture | 140 | MPa | |
| Fracture, 120 ℃ | 85.0 | MPa | |
| Fracture, 160 ℃ | 75.0 | MPa | |
| Fracture, 180 ℃ | 70.0 | MPa | |
| Fracture, 200 ℃ | 65.0 | MPa | |
| Tensile strain | |||
| fracture | 4.0 | % | |
| Fracture, 120 ℃ | 12 | % | |
| Fracture, 160 ℃ | 12 | % | |
| Fracture, 180 ℃ | 12 | % | |
| Fracture, 200 ℃ | 12 | % | |
| Bending modulus | 5800 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 45 | kJ/m² | |
| 23℃ | 50 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -40℃ | 6.0 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 290 | ℃ | |
| 1.8 MPa, unannealed | 275 | ℃ | |
| Glass transition temperature | 75.0 | ℃ | |
| Vicat Softening Temp | 290 | ℃ | |
| Melting temperature | 295 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 5.0E-5 | 1/℃ | |
| TD | 8.0E-5 | 1/℃ | |
| Relative temperature index | |||
| Electrical performance, 0.75 mm | 65.0 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.5 mm | HB |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 280 to 320 | °C | |
| Barrel middle temperature | 300 to 320 | °C | |
| Barrel front temperature | 300 to 320 | °C | |
| Nozzle temperature | 300 to 320 | °C | |
| Processing (melt) temperature | 305 to 320 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection speed | 中等偏快 | ||
| Back pressure | 2.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |