| Jackdaw PLA HW18NT6651是一种聚乳酸 (PLA)产品,。 它,在欧洲有供货。 主要特性为:环保/绿色。&& |
| Product Description | |
|---|---|
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Renewable resources |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 170℃，2.16kg | 1.2 | g/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| TD | 0.40 | % | |
| MD | 0.40 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5600 | MPa | ASTM D638, ISO 527-2 |
| tensile strength | |||
| yield | 38.0 | MPa | ASTM D638, ISO 527-2 |
| fracture | 37.0 | MPa | ISO 527-2 |
| — | 37.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638, ISO 527-2 | ||
| yield | 1.5 | % | |
| fracture | 1.5 | % | |
| Bending modulus | 4700 | MPa | ASTM D790, ISO 178 |
| bending strength | 50.0 | MPa | ASTM D790，ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 8.50 | kJ/m² | ASTM D256 |
| Charpy Unnotch Impact strength | 8.5 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 48.0 | ℃ | ASTM D648，ISO 75-2/A |
| Melting temperature | 148 | ℃ | ISO 1218，ASTM D2117 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |