| Kingfa JH710 G10是一种聚碳酸脂合金（PC 合金）材料,含有的填充物为10% 玻璃纤维增强材料。 该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 Kingfa JH710 G10的主要特性有: 阻燃/额定火焰 Flame Retardant 高强度 美观 典型应用领域包括: 电气/电子应用 印刷应用&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,Flame Characteristics,V-0 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.26 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：23℃ | 0.30 to 0.40 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 110 | J/m | ASTM D256 |
| 23℃，3.2mm | 120 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 142 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 130 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 19 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 84 | ASTM D785 | |
| tensile strength | 75.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 9.0 | % | ASTM D638 |
| Bending modulus | 4200 | MPa | ASTM D790 |
| bending strength | 105 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 230 to 250 | °C | |
| Barrel middle temperature | 235 to 260 | °C | |
| Barrel front temperature | 240 to 270 | °C | |
| Processing (melt) temperature | 235 to 260 | °C | |
| Mold temperature | 80 to 110 | °C | |
| Back pressure | 0.300 to 1.00 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |