| Starex GC-0730是一种丙烯腈丁二烯苯乙烯+ PET (ABS+PET)产品,。 它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 主要特性为:阻燃/额定火焰。 |
| Product Description | |
|---|---|
| Supplier | SAMSUNG |
| Generic | ABS+PET |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.60 to 0.80 | % | ASTM D955 |
| TD：3.2 mm | 0.60 to 0.80 | % | ASTM D955 |
| TD：2.0 mm | 0.60 to 0.80 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 560 | J/m | ASTM D256 |
| 23℃，6.4mm | 120 | J/m | ASTM D256 |
| 23℃ | 35 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 74.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm | 70.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 91.0 | ℃ | ISO 306/B50 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 91 | ASTM D785 | |
| R-level | 91 | ISO 2039-2 | |
| Tensile modulus | |||
| — | 1700 | MPa | ASTM D638 |
| — | 1750 | MPa | ISO 527-2/50 |
| Tensile strength | |||
| yield | 39.0 | MPa | ASTM D638 |
| yield | 40.0 | MPa | ISO 527-2/50 |
| fracture | 29.0 | MPa | ASTM D638 |
| fracture | 30.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 13 | % | ASTM D638 |
| fracture | 10 | % | ISO 527-2/50 |
| Bending modulus | |||
| — | 1700 | MPa | ASTM D790 |
| — | 1700 | MPa | ISO 178 |
| bending strength | |||
| — | 54.0 | MPa | ASTM D790 |
| — | 55.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | |||
| Hot air dryer | 100 | °C | |
| Vacuum dryer | 100 | °C | |
| Drying time | |||
| Hot air dryer | 2.0 to 3.0 | hr | |
| Vacuum dryer | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.050 | % | |
| Temperature at the rear of the barrel | 210 | °C | |
| Temperature in the middle of the barrel | 220 to 230 | °C | |
| Front temperature of material barrel | 240 to 250 | °C | |
| Nozzle temperature | 250 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Injection pressure | 49.0 to 245 | MPa | |
| Back pressure | 0.490 to 1.96 | MPa | |
| Screw speed | 50 to 150 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |