| Clearflex FG B0 is a linear low density polyethylene, with antioxidants, suitable for blown film technology. The product is characterised by a very low density and high molecular weight. Films made by Clearflex FG B0 are highly transparent, have a good sealing, even at low temperature, and excellent mechanical properties. Main Application Clearflex FG B0 is recommended to produce blown stretch film and is used in blend or coextrusion because of its unique properties.&& |
| Product Description | |
|---|---|
| Generic | VLDPE |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good heat sealing,Food contact compliance,Inoxidizability,High molecular weight,Low density,Low temperature heat sealing |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.911 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.90 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Self dynamic, blow molded film | > 0.50 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | 10 to 50µm | ||
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, blow molded film | 90.0 | MPa | ISO 527-3 |
| 1% secant, TD, blow molded film | 100 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, blow molded film | 7.00 | MPa | ISO 527-3 |
| TD, yield, blow molded film | 7.00 | MPa | ISO 527-3 |
| MD, fracture, blow molded film | 40.0 | MPa | ISO 527-3 |
| TD, fracture, blow molded film | 32.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, blow molded film | 500 | % | ISO 527-3 |
| TD, fracture, blow molded film | 800 | % | ISO 527-3 |
| Drop hammer impact | |||
| Blown film | 250 | g | ISO 7765-1 |
| tear strength | ISO 6383-2 | ||
| MD | 70.0 | kN/m | ISO 6383-2 |
| TD | 110.0 | kN/m | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 88.0 | ℃ | ISO 306/A |
| Melting temperature | 120 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, blow molded film | 65 | ASTM D2457 | |
| Haze | |||
| Blown film | 6.0 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 200 to 230 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |