| Bormed RD808CF-11 is a random copolymer with high ethylene content. This grade is suitable for the manufacturing of non-oriented cast films on chill roll process and blown films on tubular water quenching process as well as injection moulding and ISBM (2-stage process) for ampoules and bottles.&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,Random copolymer,Weight distribution |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 8.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | |||
| 23℃ | 700 | MPa | ISO 178 |
| friction coefficient | > 0.70 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-3 | ||
| MD | 400 | MPa | ISO 527-3 |
| TD | 400 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD | 30.0 | MPa | ISO 527-3 |
| TD | 30.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture | 540 | % | ISO 527-3 |
| TD, fracture | 610 | % | ISO 527-3 |
| Instrumented Puncture Test（Total Penetration Energy） | 300 | J/cm | ISO 7765-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 140 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20° | > 140 | ASTM D2457 | |
| Haze | < 0.50 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 50% Relative Humidity |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |