ACRYLITE® Hi-Gloss NTA-5

About
ACRYLITE® Hi-Gloss NTA-5 black is an amorphous thermoplastic molding compound, based on impact-modified polymethyl methacrylate (PMMA). Properties ACRYLITE® molding compounds have the following typical properties: high weather resistance brilliant appearance 100% recyclable ACRYLITE® Hi-Gloss NTA-5 black is characterized by the following additional properties: highest breaking strength and impact strength increased heat resistance improved resistance to stress cracking balanced property profile Application areas are: Add-on automotive body parts, pillar-trims, mirror housings, trim parts at front – and rear end, etc.&&

About

ACRYLITE® Hi-Gloss NTA-5 black is an amorphous thermoplastic molding compound, based on impact-modified polymethyl methacrylate (PMMA). Properties ACRYLITE® molding compounds have the following typical properties: high weather resistance brilliant appearance 100% recyclable ACRYLITE® Hi-Gloss NTA-5 black is characterized by the following additional properties: highest breaking strength and impact strength increased heat resistance improved resistance to stress cracking balanced property profile Application areas are: Add-on automotive body parts, pillar-trims, mirror housings, trim parts at front – and rear end, etc.&&

Product Description
Supplier	ROHM
Generic	PMMA
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,Good surface appearance,High impact resistance,Renewable resources,Amorphous
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.16	g/cm³	ISO 1183
Melt Volume Rate
230℃，3.8 kg	1.30	cm³/10min
260℃，3.8 kg	8.00	cm³/10min
Water absorption rate
Saturation, 23 ℃	1.5	%
Equilibrium, 23 ℃, 50% RH	0.50	%

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	2100	MPa	ISO 527-1-2
tensile strength
yield	54.0	MPa	ISO 527-2/50
Tensile strain
yield	5.0	%	ISO 527-2/50
Nominal tensile fracture strain	48	%	ISO 527-2

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength
23℃	110	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	102	℃	ISO 75-2/B
1.8 MPa, unannealed	96.0	℃	ISO 75-2/A
Glass transition temperature	113	℃	ISO 11357-2
Vicat Softening Temp
B50	103	℃	ISO 306
Linear coefficient of thermal expansion
MD：0~50℃	1.1E-4	1/℃	ISO 11359-2

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
1.60 mm	HB		IEC 707

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	> 4.0	hr
Processing (melt) temperature	230 to 260	°C
Mold temperature	60 to 80	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.