| About |
|---|
| Geon™ HTX M6309 is a Polyvinyl Chloride Alloy (PVC Alloy) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Geon™ HTX M6309 include outdoor applications, construction applications, electrical/electronic applications and wire & cable. Characteristics include: Flame Rated High Flow Impact Resistant&& |
| Product Description | |
|---|---|
| Generic | PVC alloy |
| Material Status | Commercial: Active |
| Features | V-0,High liquidity,low-temperature impact resistance,5VA |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ASTM D792 |
| Spiral flow length | 63.5 | cm | |
| Shrinkage rate | |||
| MD | 0.20 to 0.50 | % | ASTM D955 |
| Outdoor applicability | |||
| grey | f1 | UL 746C | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256A | ||
| -40 ℃, 3.2mm, injection molding | 210 | J/m | ASTM D256-A |
| -18 ℃, 3.2mm, injection molding | 590 | J/m | ASTM D256-A |
| 0 ℃, 3.2mm, injection molding | 750 | J/m | ASTM D256-A |
| 23 ℃, 3.2mm, injection molding | 850 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.35 mm | 75.0 | ℃ | ASTM D648 |
| 0.45 MPa, annealed, 6.35 mm | 83.9 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.35 mm | 67.8 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 6.35 mm | 73.9 | ℃ | ASTM D648 |
| Relative temperature index | 50.0 | ℃ | UL 746 |
| Electrical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 2.00 mm, all colors | V-0 | UL 94 | |
| 3.00 mm, all colors | 5VA | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| QUV aging testing machine | 0.50 | % |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 75 | ASTM D2240 | |
| Tensile modulus | 1650 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 29.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 56 | % | ASTM D638 |
| Bending modulus | 1650 | MPa | ASTM D790 |
| bending strength | 48.3 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| drying temperature | 68 | °C | |
| Drying time | 2.0 | hr | |
| Melt Temperature | 202 to 207 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 351 Lamp, All Colors, detla E (CIE), 24 hrs light, 300 hrs, No Moisutre |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |