| Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose PA6 injection molding. It possesses the combination of strength and toughness and has excellent chemical and abrasion resistance. The heat stabilizer system extends the retention of properties at the more elevated temperatures. Excellent in filling thin walls or areas. Applications Ultramid 8202 HS is generally recommended for drapery hardware, gears, fittings, furniture casters, bearings, handles, clips, fasteners and thin parts.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Low Viscosity,Good wear resistance,Solvent resistance,Heat Stabilized,Homopolymer,V-2 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.2 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 9.5 | % | ISO 62 |
| saturated | 9.5 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 2.7 | % | ISO 62 |
| Balance, 50% RH | 2.7 | % | ASTM D570 |
| 24hr | 1.6 | % | ASTM D570 |
| 23℃，24hr | 1.6 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.5 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 51 | kJ/m² | ISO 179 |
| 23℃ | No Break | ISO 179 | |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃ | 48 | J/m | ASTM D256 |
| 23℃ | 58 | J/m | ASTM D256 |
| Falling impact resistance | |||
| 23℃ | 142 | J | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 65.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 60.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 150 | ℃ | ISO 75-2/B |
| 0.45 MPa, unannealed | 178 | ℃ | ASTM D648 |
| Melting peak temperature | 220 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| MD | 8.3E-5 | 1/℃ | ASTM E831 |
| 0.71 mm | 130 | ℃ | UL 746 |
| 1.5 mm | 130 | ℃ | UL 746 |
| 3.0 mm | 130 | ℃ | UL 746 |
| 6.0 mm | 130 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 0.71 mm | 95.0 | ℃ | UL 746 |
| 3.0 mm | 105 | ℃ | UL 746 |
| 1.5 mm | 105 | ℃ | UL 746 |
| 6.0 mm | 105 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| 1.50 mm | > 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric strength | 37 | kV/mm | IEC 60243-1 |
| 1.5 mm | 22 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.71 mm | V-2 | UL 94 | |
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 | |
| 6.00 mm | V-2 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | ||
| 23℃ | 2700 | MPa | ISO 527-2 |
| 80℃ | 485 | MPa | ISO 527-2 |
| 120℃ | 360 | MPa | ISO 527-2 |
| 150℃ | 290 | MPa | ISO 527-2 |
| tensile strength | ASTM D638 | ||
| Yield, -40 ℃ | 126 | MPa | ASTM D638 |
| Yield, 23 ℃ | 79.0 | MPa | ASTM D638 |
| Yield, 80 ℃ | 35.0 | MPa | ASTM D638 |
| Yield, 121 ℃ | 25.0 | MPa | ASTM D638 |
| tensile strength | ISO 527-2 | ||
| Fracture, 23 ℃ | 75.0 | MPa | ASTM D638 |
| Yield, -40 ℃ | 126 | MPa | ISO 527-2 |
| Yield, 23 ℃ | 78.0 | MPa | ISO 527-2 |
| Yield, 80 ℃ | 35.0 | MPa | ISO 527-2 |
| Yield, 120 ℃ | 25.0 | MPa | ISO 527-2 |
| Yield, 150 ℃ | 20.0 | MPa | ISO 527-2 |
| Tensile strain | ASTM D638 | ||
| Fracture, 23 ℃ | 55 | % | ASTM D638 |
| Yield, 23 ℃ | 4.0 | % | ISO 527-2 |
| Yield, 23 ℃ | 4.0 | % | ASTM D638 |
| Yield, 80 ℃ | 42 | % | ASTM D638 |
| Yield, 121 ℃ | 36 | % | ASTM D638 |
| Nominal tensile fracture strain | |||
| 23℃ | 25 | % | ISO 527-2 |
| Bending modulus | ASTM D790 | ||
| 23℃ | 2400 | MPa | ISO 178 |
| -40℃ | 3010 | MPa | ASTM D790 |
| 23℃ | 2830 | MPa | ASTM D790 |
| 65℃ | 500 | MPa | ASTM D790 |
| 90℃ | 350 | MPa | ASTM D790 |
| 121℃ | 305 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| 23℃ | 85.0 | MPa | ISO 178 |
| -40℃ | 170 | MPa | ASTM D790 |
| 23℃ | 108 | MPa | ASTM D790 |
| 65℃ | 30.0 | MPa | ASTM D790 |
| 90℃ | 20.0 | MPa | ASTM D790 |
| 121℃ | 17.0 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 119 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 240 to 285 | °C | |
| Mold temperature | 65 to 80 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |