| Product Description | |
|---|---|
| Supplier | SUQING |
| Generic | PCTG |
| Material Status | Commercial: Negative |
| Features | Quick molding cycle,Amorphous,High impact resistance,Hydrolysis stability,Solvent resistance,Food contact compliance,Excellent Processability,Durability,Good stripping performance,High Heat Resistance,Low Viscosity,Good Clarity,High liquidity,Good flexibility |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180 | ||
| 23℃ | 860 | J/m | ASTM D256 |
| 23℃ | No Break | ASTM D4812 | |
| -40℃ | 11 | kJ/m² | ISO 180 |
| 23℃ | 83 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 81.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 94.0 | ℃ | ASTM D648 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| total | 91.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 1600 | MPa | ISO 527-2 |
| 23℃ | 1580 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 23 ℃ | 52.0 | MPa | ASTM D638 |
| Fracture, 23 ℃ | 49.0 | MPa | ISO 527-2 |
| Yield, 23 ℃ | 44.0 | MPa | ISO 527-2 |
| Yield, 23 ℃ | 43.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 210 | % | ASTM D638 |
| Fracture, 23 ℃ | 150 | % | ISO 527-2 |
| Yield, 23 ℃ | 7.0 | % | ISO 527-2 |
| Yield, 23 ℃ | 7.0 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 1580 | MPa | ASTM D790 |
| 23℃ | 1500 | MPa | ISO 178 |
| bending strength | |||
| Yield, 23 ℃ | 64.0 | MPa | ASTM D790 |
| 23℃ | 60.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 111 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 88 | °C | null |
| Drying time | 4.0 to 6.0 | hr | null |
| Processing (melt) temperature | 260 to 282 | °C | null |
| Mold temperature | 38 to 66 | °C | null |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |