| About |
|---|
| This high density polyethylene is tailored for blown film applications that require: Outstanding water vapor barrier properties Good film strength and toughness for a homopolymer Paper-like film texture Exceptional drawdown Excellent stiffness Typical blown film applications include: Food packaging Coextrusions Overwraps Deli wrap Moisture barrier films&& |
| Product Description | |
|---|---|
| Supplier | Chevron Phillips |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good dissection,Moisture resistance,High density,Homopolymer |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.962 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Blown film | 0.25 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | |||
| 1% secant, MD: 25 µ m, blow molded film | 1080 | MPa | |
| 1% secant, TD: 25 µ m, blow molded film | 1370 | MPa | |
| tensile strength | |||
| MD, fracture, 25 µ m, blow molded film | 42.0 | MPa | |
| TD, fracture, 25 µ m, blow molded film | 26.0 | MPa | |
| Tensile strain | |||
| MD, fracture, 25 µ m, blow molded film | 490 | % | |
| TD, fracture, 25 µ m, blow molded film | 550 | % | |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 50 | g | ASTM D1709 |
| Elmandorf tear strength | |||
| MD: 25 µ m, blow molded film | 19 | g | |
| TD: 25 µ m, blow molded film | 210 | g | |
| Oxygen transfer rate | |||
| 25 µ m, blow molded film | 2000 | cm³/m²/24 hr | ASTM D3985 |
| Water vapor transmittance | |||
| 25 µ m, blow molded film | 4.0 | g/m²/24 hr | ASTM F1249 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |