| Safrene® H 4765 High Density Polyethylene Resin is a bimodal medium molecular mass grade with good processing properties. Safrene® H 4765 High Density Polyethylene Resin is recommended for small part blow moulding applications up to 20 litres in volume where good impact excellent stiffness and environmental stress-crack resistance are required. Typical Applications Milk and Fruit juice containers Cosmetics, toiletries and household care products General purpose containers&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Excellent Processability,High impact resistance,Food contact compliance,High density,Bimodal molecular weight distribution,High ESCR |
| Availabilitys | Africa & Middle East |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.958 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 0.33 | g/10min | ISO 1133 |
| 190℃，5.0kg | 1.4 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 10% non-ionic surfactant, F50 | 150 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30 ℃, molded | 9.0 | kJ/m² | ISO 179 |
| 23 ℃, molded | 13 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 128 | ℃ | ISO 306/A50 |
| B50 | 78.0 | ℃ | ISO 306 |
| Crystallization peak temperature | |||
| DSC | 130 to 133 | ℃ | ISO 3146 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blow molding mold temperature | 190 to 200 | ℃ | |
| Blow Molding Melt Temperature | 190 to 200 | ℃ | |
| Blowing molding temperature | |||
| Feed Zone | 160 to 180 | ℃ | |
| Zone | 170 to 190 | ℃ | |
| Zone | 180 to 200 | ℃ | |
| Zone | 180 to 190 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 64 | ISO 868 | |
| tensile strength | ISO 527-2/50 | ||
| Yield, molding | 29.0 | MPa | ISO 527-2/50 |
| Fracture, molded | 34.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, molded | > 600 | % | ISO 527-2/50 |
| Bending modulus | 1450 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Unannealed |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |