| 30% Glass Reinforced, Flame Retardant (halogen free)&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | V-0,Halogen free,Flame Characteristics |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.60 | % | ISO 294-4 |
| MD | 0.20 | % | ISO 294-4 |
| Water Absorption | |||
| Equilibrium, 23 ℃, 50% RH | 1.7 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Broken BRK | 135 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK | 2.0 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 50 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 205 | ℃ | ISO 75-2/A |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared Tracking Index | — | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | IEC 60695-11-10, -20 | ||
| 0.8 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.6 mm | V-0 | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index GWFI | IEC 60695-2-12 | ||
| 0.80 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.6 mm | 960 | ℃ | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (GWIT) | IEC 60695-2-13 | ||
| 1 mm | 775 | ℃ | IEC 60695-2-13 |
| 1.6 mm | 775 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature Zone 1 | 230 to 250 | °C | |
| Middle Temperature Zone 2 | 230 to 260 | °C | |
| Front Temperature Zone 3 | 230 to 260 | °C | |
| Nozzle temperature | 250 to 280 | °C | |
| Melt Temperature | 245 to 270 | °C | |
| Mold Temperature | 40 to 80 | °C | |
| Injection speed | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |