| About |
|---|
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Good Clarity,High liquidity,High Heat Resistance,Good surface appearance,Excellent Processability |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 6.3 | g/10min | ASTM D1238 |
| 200℃，5.0kg | 6.3 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 3.20 mm | 2700 | MPa | ISO 527-2/5 |
| 3.20 mm | 2700 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 3.20 mm | 27.0 | MPa | ASTM D638 |
| Fracture, 3.20 mm | 27.0 | MPa | ISO 527-2/5 |
| Yield, 3.20 mm | 33.0 | MPa | ISO 527-2/5 |
| Yield, 3.20 mm | 33.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | > 20 | % | ISO 527-2/5 |
| Fracture, 3.20 mm | > 20 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2600 | MPa | ASTM D790 |
| 3.20 mm | 2600 | MPa | ISO 178 |
| bending strength | |||
| 3.20 mm | 62.0 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm | 62.0 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 72.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 72.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 100 | ℃ | ASTM D1525 6 |
| Vicat Softening Temp | 100 | ℃ | ISO 306/A120 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60°，Thermoformed | 60 | ASTM D523 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |