| MonoSol AF L336 is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol AF’s proprietary blown film technology. MonoSol AF L336 is a cold water-soluble film with good solubility, toughness and cold crack resistance. In bag form, MonoDose™ L336 film is a leading candidate for powder delivery systems with no special requirements or contraindications. It can also be used for special applications such as self adhesive labels, lamination, and soluble dams for inert gas welding of SS pipe. Available thickness range is 20 micron (0.8 mil) to 80 micron (3.1 mil).&& |
| Product Description | |
|---|---|
| Generic | PVOH |
| Material Status | Commercial: Active |
| Features | Good flexibility,Antifreeze,Biodegradable,Good tear strength,Water soluble |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| film | Nominal value | Unit | Test method |
| film thickness | |||
| test | 32 | µm | |
| Secant modulus | |||
| 10%，MD：32 µm | 103 | MPa | |
| 100%，MD：32 µm | 31.0 | MPa | |
| 10%，TD：32 µm | 88.9 | MPa | |
| 100%，TD：32 µm | 18.6 | MPa | |
| tensile strength | |||
| MD, fracture, 32 µ m | 46.9 | MPa | ASTM D882 |
| TD, fracture, 32 µ m | 40.0 | MPa | ASTM D882 |
| MD，32 µm | 46.9 | MPa | ISO 527-3 |
| TD，32 µm | 40.0 | MPa | ISO 527-3 |
| Tensile strain | |||
| MD, fracture, 32 µ m | 200 | % | |
| TD, fracture, 32 µ m | 300 | % | |
| dosage | |||
| density at 1.25 g/cc，32.0 µm | 25.0 | m²/kg | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |