| ALCUDIA® PE034/A is a low density polyethylene grade, produced by high pressure autoclave technology, suitable for blown or cast film applications. This material offers easy processability and good balance of mechanical and optical properties. It contains antioxidant additive and antiblock additives. TYPICAL APPLICATIONS General packaging film. Shrink film with high mechanical resistance. Heavy duty sacks. Recommended melt temperature range from 190-220°C. Processing conditions should be optimised for each production line.&& |
| Product Description | |
|---|---|
| Supplier | REPSOL |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Optical performance,High anti-blocking,Food contact compliance,Inoxidizability |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.30 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Self dynamic, blow molded film | > 0.50 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 200 | µm | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 200 µ m, blow molded film | 11.0 | MPa | ISO 527-3 |
| TD, yield, 200 µ m, blow molded film | 11.0 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 200 µ m, blow molded film | 21.0 | MPa | ISO 527-3 |
| TD, fracture, 200 µ m, blow molded film | 19.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 200 µ m, blow molded film | 550 | % | ISO 527-3 |
| TD, fracture, 200 µ m, blow molded film | 650 | % | ISO 527-3 |
| Drop hammer impact | |||
| 200 µ m, blow molded film | 700 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD: 200 µ m, blow molded film | 6.0 | N | ISO 6383-2 |
| TD: 200 µ m, blow molded film | 9.5 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 94.0 | ℃ | ISO 306/A |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 200 µ m, blow molded film | 55 | ASTM D2457 | |
| Haze | |||
| 200 µ m, blow molded film | 20 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |