| TUFLIN™ HS-7001 NT 7 Linear Low Density Polyethylene Resin is an antioxidant modified ethylene-hexene-1 copolymer resin designed for slot cast extrusion. It is supplied in pelleted form. Films produced from HS-7001 NT 7 exhibit high clarity, high tensile strength, high elongation and good puncture resistance. This resin has outstanding drawdown capability. Main Characteristics: Designed for slot cast thin film applications including stretch and cling wraps High clarity Superior toughness Complies with U.S. FDA 21 CFR 177.1520(c) 3.1a Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.917 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.2 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 25 µ m | 165 | MPa | ASTM D882 |
| 1% secant, TD: 25 µ m | 172 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 25 µ m | 32.4 | MPa | ASTM D882 |
| TD, yield, 25 µ m | 29.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 25 µ m | 750 | % | ASTM D882 |
| TD, fracture, 25 µ m | 830 | % | ASTM D882 |
| Drop hammer impact | |||
| 25 µm | 120 | g | ASTM D1709-A |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：25 µm | 370 | g | ASTM D1922 |
| TD：25 µm | 500 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，25.4 µm | 90 | ASTM D523 | |
| Haze | |||
| 25.4 µm | 2.5 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 266 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method B |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |