| About |
|---|
| Resin of LTP CT-1200 serials is a kind of engineering plastic with high performance based on PPS. For its outstanding thermal transmittance and insulation ability, life-time service around 180-220°C, the materials are suitable for produce varied shell or capsulation for electric heating element and electric appliance element with high elimination of heat.&& |
| Product Description | |
|---|---|
| Supplier | Letian |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | High Heat Resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.62 | g/cm³ | GB/T 1033 |
| Shrinkage rate | |||
| 4.0 mm | 0.30 to 0.60 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.20 to 0.40 | % | GB/T 1034 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 100 | MPa | GB/T 1040 |
| Tensile strain | |||
| fracture | 1.2 | % | GB/T 1040 |
| Bending modulus | 12000 | MPa | GB/T 1042 |
| bending strength | 120 | MPa | GB/T 1042 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| specific heat | 1200 | J/kg/℃ | ASTM E1461 |
| Thermal conductivity coefficient | 5.0 | W/m/K | ASTM E1461 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+12 | ohms·cm | GB/T 1410 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 80x80x4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |