Santoprene™ 8211-55B100

About
A soft, colorable, specialty, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It is especially formulated to bond to ABS, PS, PC, PMMA, ASA, PET and PPO/PS blends for applications where hard/soft combinations are required. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It is polyolefin based and recyclable within the manufacturing stream.&&

Product Description
SupplierCelanese
Material StatusCommercial: Active
FeaturesHB
AvailabilitysAsia Pacific

Technical Data
PHYSICALNominal valueUnitTest method
Density1.04g/cm³ASTM D792
Density1.04g/cm³ISO 1183

MECHANICALNominal valueUnitTest method
Tensile Strain
TD, fracture, 23 ℃600%ASTM D412
TD, fracture, 23 ℃600%ISO 37
125℃，70 hr55%ISO 815
125℃，70 hr55%ASTM D395B

MECHANICALNominal valueUnitTest method
Shore hardness
Shore A, 15 seconds, 23 ℃53 ISO 868

Aging propertyNominal valueUnitTest method
Change in Tensile Strength in Air ASTM D573
100℃，168 hr-28%ASTM D573
125℃，168 hr-61%ASTM D573
Change in Tensile Strength in Air ISO 188
100℃，168 hr-28%ISO 188
125℃，168 hr-61%ISO 188
Change in Ultimate Elongation in Air ASTM D573
100℃，168 hr-14%ASTM D573
125℃，168 hr-70%ASTM D573
Change in Tensile Stress at Break in Air ISO 188
100℃，168 hr-14%ISO 188
125℃，168 hr-70%ISO 188
Change in Durometer Hardness in Air ASTM D573
Shaw A, 100 ℃, 168 hr-4.0 ASTM D573
Shaw A, 125 ℃, 168 hr8.0 ASTM D573
Change in Shore Hardness in Air ISO 188
Shaw A, 100 ℃, 168 hr-4.0 ISO 188
Shaw A, 125 ℃, 168 hr8.0 ISO 188
Change in Tensile Strength ASTM D471
23℃，168 hr，in Ethanol，95%-17%ASTM D471
23℃，168 hr，in Hydrochloric Acid，10%-1.0%ASTM D471
23℃，168 hr，in IRM 903 Oil-85%ASTM D471
23℃，168 hr，in Sodium Hydroxide，50%1.0%ASTM D471
23 ℃, 168 hr, in water2.0%ASTM D471
Change in Tensile Strength ISO 1817
23℃，168 hr，in Ethanol，95%-17%ISO 1817
23℃，168 hr，in Hydrochloric Acid，10%-1.0%ISO 1817
23℃，168 hr，in IRM 903 Oil-85%ISO 1817
23℃，168 hr，in Sodium Hydroxide，50%1.0%ISO 1817
23 ℃, 168 hr, in water2.0%ISO 1817
Change rate of ultimate elongation ASTM D471
23℃，168 hr，in Ethanol，95%-3.0%ASTM D471
23℃，168 hr，in Hydrochloric Acid，10%-9.0%ASTM D471
23℃，168 hr，in IRM 903 Oil-68%ASTM D471
23℃，168 hr，in Sodium Hydroxide，50%-7.0%ASTM D471
23 ℃, 168 hr, in water-12%ASTM D471
Change in tensile stress during fracture ISO 1817
23℃，168 hr，in Ethanol，95%-3.0%ISO 1817
23℃，168 hr，in Hydrochloric Acid，10%-9.0%ISO 1817
23℃，168 hr，in IRM 903 Oil-68%ISO 1817
23℃，168 hr，in Sodium Hydroxide，50%-7.0%ISO 1817
23 ℃, 168 hr, in water-12%ISO 1817
Change rate of Shore hardness ASTM D471
Shore A, 23 ℃, 168 hr, in ethanol, 95%2.0 ASTM D471
Shore A, 23 ℃, 168 hr, in hydrochloric acid, 10%4.0 ASTM D471
Shaw A, 23 ℃, 168 hr, in IRM 903 oil-33 ASTM D471
Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50%4.0 ASTM D471
Shaw A, 23 ℃, 168 hr, in water5.0 ASTM D471
Change rate of Shore hardness ISO 1817
Shore A, 23 ℃, 168 hr, in ethanol, 95%2.0 ISO 1817
Shore A, 23 ℃, 168 hr, in hydrochloric acid, 10%4.0 ISO 1817
Shaw A, 23 ℃, 168 hr, in IRM 903 oil-33 ISO 1817
Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50%4.0 ISO 1817
Shaw A, 23 ℃, 168 hr, in water5.0 ISO 1817

FLAME CHARACTERISTICSNominal valueUnitTest method
Flame Class Rating UL 94
1.10 mmHB UL 94
2.90 mmHB UL 94

Notes
1. Typical properties: these are not to be construed as specifications.
2. Type 1
3. Type A
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.