| Good flowing ASA/PA 6-blend with high UV-stability. Material with low gloss level. Applications: automotive interior. (Former name: M/MW UV K2325) |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | ASA+PA |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,Low odor,Low Gloss |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | |
| Melt Volume Rate | |||
| 250℃，5 kg | 3.00 | cm³/10min | |
| 260℃，5 kg | 12.0 | cm³/10min | |
| Shrinkage rate | 0.80 to 1.2 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 18 | kJ/m² | |
| 23℃ | 100 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 99.0 | ℃ | |
| 1.8 MPa, unannealed | 56.0 | ℃ | |
| Vicat Softening Temp | |||
| — | 205 | ℃ | |
| — | 117 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | |
| Volume resistivity | > 1.0E+15 | ohms·cm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 2.0 mm | 21 | mm/min | |
| Flame retardant level | |||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness (H 358/30) | 100 | MPa | |
| Tensile modulus | 1800 | MPa | |
| Tensile stress (yield) | 44.0 | MPa | |
| Tensile strain | |||
| yield | 3.2 | % | |
| Nominal tensile fracture strain | > 100 | % |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 230 to 270 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |